Preparation and characterization of platinum doped porous titania nanoparticles for photocatalytic oxidation of carbon monoxide
Preparation and characterization of platinum doped porous titania nanoparticles for photocatalytic oxidation of carbon monoxide
 
الموضوع : كيمياء 
لغة الوثيقة : الانجليزية 
المستخلص : TiO 2 samples doped with platinum oxide were obtained by using a sol-gel low temperature approach. The photocatalytic oxidation of CO in the presence of O 2 was monitored to study the influence of the Pt doping on the photocatalytic degradation performance of TiO 2. The obtained results were compared with those obtained with TiO 2 Degussa (P-25). Photocatalytic studies of the prepared mesoporous Pt/TiO 2 nanoparticles for the photooxidation of CO revealed notable photocatalytic activity, which was 3 times higher than that of Pt photodeposited onto commercial TiO 2 Degussa P-25. Also quantum yield for CO 2 formation for mesoporous Pt/TiO 2 calcined at 500 °C is higher than that of Pt photodeposited onto commercial TiO 2 Degussa P-25 by about three times. The structure and textural properties Pt/TiO 2 were studied by X-ray powder diffraction (XRD), N 2 adsorption (BET), Transmission electron microscopy (TEM) and UV. 
ردمد : 0925-8388 
اسم الدورية : Journal of Alloys and Compounds 
المجلد : 509 
العدد : 41 
سنة النشر : 1432 هـ
2011 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Wednesday, April 18, 2012 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
رضا محمدي محمدMohamed, R Mباحثدكتوراهredama123@yahoo.com
الهام شفيق أعظمAazam, Elham Sباحثدكتوراهwayfield8@yahoo.com

الملفات

اسم الملفالنوعالوصف
 32906.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث