Synthesis characterization and magnetic properties of Cr-substituted NiCuZn nanocrystalline ferrite
Synthesis characterization and magnetic properties of Cr-substituted NiCuZn nanocrystalline ferrite
 
الموضوع : كيمياء 
لغة الوثيقة : الانجليزية 
المستخلص : Egg-white method was used to produce nanocrystalline Cr-substituted NiCuZn ferrites; Ni0.50Cu0.25Zn0.25Fe 2-xCrxO4 (0.0 ≤ x ≤ 1.0) from stoichiometric mixture of their respective metal nitrate. The structural, morphological and magnetic properties of the products were determined by X-ray powder diffractometry (XRD), Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). The average crystallite sizes obtained from XRD were between 15 and 25 nm. Magnetization measurements indicated that when the Cr substitution increases the saturation magnetization decreases due to the magnetic character of the chromium ions which prefers octahedral site occupation. The coercivity was found to change proportionally with the particle sizes of the investigated ferrites. 
ردمد : 0925-8388 
اسم الدورية : Journal of Alloys and Compounds 
المجلد : 506 
العدد : 1 
سنة النشر : 1431 هـ
2010 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Sunday, October 9, 2011 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
W A BayoumyBayoumy, W Aباحثدكتوراه 
محمد عبدالفتاح جبلGabal, Mohamed Aباحثدكتوراهmgabalabdonada@yahoo.com

الملفات

اسم الملفالنوعالوصف
 31002.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث